Doping gamma-Fe(2)O(3) nanoparticles with Mn(III) suppresses the transition to the alpha-Fe(2)O(3) structure

Here we report on a mixed oxide system, gamma-Fe2O3 nanoparticles doped with Mn(III), where the transition from the cubic to the more stable hexagonal alpha-Fe2O3 structure is suppressed. When amorphous Fe2O3 is heated at 300 degrees C for 3 h, ferrimagnetic gamma-Fe2O3 is observed as the sole product. On the other hand, when the temperature is raised to 500 degrees C, one observes only antiferromagnetic alpha-Fe2O3 as the product. However, upon doping with 8.5 wt % Mn(III), the amorphous nanoparticles crystallized to mainly the gamma-Fe2O3 matrix after heating at 500 degrees C for 3 h, and need to be heated to >650 degrees C for the complete transition to the alpha-Fe2O3 structure to take place.