N-methacryloly-(L)-histidinemethylester carrying a pseudospecific affinity sorbent for immunoglobulin-G isolation...

N-methacryloly-(L)-histidinemethylester (MAH) as a pseudospecific ligand was synthesized by using methacryloyl chloride and histidine. Spherical beads with an average size of 63-75 microm were obtained by suspension polymerization of ethylene glycol dimethacrylate (EGDMA), 2-hydroxyethyl methacrylate (HEMA) and MAH conducted in an aqueous dispersion medium. The specific surface area of the beads was found to be 18.3 m2/g. Poly(EGDMA-HEMA-MAH) beads were used in the separation of immunoglobulin-G (HIgG) from aqueous solutions and/or human plasma in a packed-bed column system. HIgG adsorption capacity of the beads decreased with an increase in the flow-rate of plasma. The maximum HIgG adsorption on the poly(EGDMA-HEMA-MAH) sorbents was observed at pH 7.4. HIgG adsorption onto the poly(EGDMA-HEMA) sorbents was negligible. Higher adsorption values (up to 135 mg/g) were obtained when the poly(EGDMA-HEMA-MAH) sorbents were used from aqueous solutions. HIgG adsorption increased with decreasing temperature and the maximum adsorption achieved at 4 degrees C. MAH incorporation significantly affected HIgG adsorption capacity (135 mg/g). Higher amounts of HIgG were adsorbed from human plasma (up to 165 mg/g). Adsorption capacities of other blood proteins were obtained as 8.7 mg/g for fibrinogen and 14.6 mg/g for albumin. The total protein adsorption was determined as 191 mg/g. The pseudospecific affinity beads allowed one-step separation of HIgG from human plasma. HIgG molecules could be repeatedly adsorbed and desorbed with these sorbents without noticeable loss in their HIgG adsorption capacity.