The effect of carbon surface chemical composition on the adsorption of acetanilide

The study of acetanilide adsorption-desorption performed at three temperatures (300, 310, and 320 K) and at two pH levels (7.0 and 1.5) on the series of D43/1 carbons (initial and modified with HNO3, fuming H2SO4, and gaseous NH3) is reported. Sorption data are additionally supplemented with the results of thermal analysis and calorimetric and kinetic measurements. It is shown that, generally, acetanilide adsorption at the neutral pH level is reversible (only on the more acidic carbons and at the lowest temperature does hysteresis occur due to the formation of hydrogen bonds with surface OH groups), and it decreases for the chemically modified carbons. In contrast, at the acidic pH level acetanilide adsorption is irreversible. A mechanism of irreversibility is proposed and it is shown that hysteresis is caused by the chemical reaction between the nucleophile (carbon) and the protonized acetanilide molecules. For all studied carbons, at the acidic pH level, adsorption increases and this is caused by the weakly basic character of acetanilide molecule. Adsorption results are described applying adsorbability and Dubinin-Astakhov, quasi-Freundlich and solution analogue of the Toth adsorption isotherm equations. Using the kinetic data, the effective diffusion coefficients and the energy of diffusion are calculated. It is shown that the diffusion is mainly a surface process, and the contribution of the pore diffusion increases with the rise in temperature. By applying different correlations between the parameters obtained from the theoretical description of experimental data and those characterizing the chemical composition of the studied carbons, the role of the latter in the adsorption and kinetics of acetanilide adsorption is determined.