Analysis of three-dimensional sinter shrinkage of copings made from alumina in an innovative direct shaping process

Eva-Maria Brick1, Heike Rudolph, Jens Arnold

  • 1Department of Prosthodontics, Medical Faculty, University Hospital Carl Gustav Carus, Dresden University of Technology, Fetscherstr. 74, 01307 Dresden, Germany. eva-maria.brick@mailbox.tu-dresden.de

Computerized Medical Imaging and Graphics : the Official Journal of the Computerized Medical Imaging Society
|April 15, 2004
PubMed

More Related Videos

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography06:53

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography

Published on: January 25, 2019

Fused Filament Fabrication (FFF) of Metal-Ceramic Components08:43

Fused Filament Fabrication (FFF) of Metal-Ceramic Components

Published on: January 11, 2019

Related Concept Videos

Shrinkage in Concrete01:27

Shrinkage in Concrete

Shrinkage in concrete is primarily due to water loss from evaporation, hydration of cement, or carbonation, leading to a reduction in volume. The volumetric contraction results in volumetric strain in concrete. However, in practice, shrinkage is measured as linear strain, which is one-third of the volumetric strain.
When concrete is still in its plastic state, it can undergo a decrease in volume by about 1% of its absolute volume. This decrease is known as plastic shrinkage. It arises either...
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...