The bonding effectiveness of five luting resin cements to the IPS Empress 2 all ceramic system
V Bookhan1, A R M Essop, I C Du Preez
1Department of Restorative Dentistry, School of Dentistry, University of Pretoria, Gauteng, South Africa. definitesol@hotmail.com
Background:
Variolink II is the only resin cement used for bonding IPS (Ivoclar Porcelain System) Empress 2 ceramic restorations. Alternative luting resin cements need to be investigated for their bonding effectiveness with the IPS Empress 2 ceramic.
Objectives:
To determine the shear bond strength (SBS) and the effect of thermocycling, on the bonding effectiveness, of five resin cements to IPS Empress 2 ceramic.
Materials And Methods:
The projecting surfaces of one hundred ceramic discs were ground wet on silicone carbide paper. The specimens were divided into 5 groups of 20. The resin cements were bonded to the prepared ceramic surfaces, in the form of a stub. The specimens were stored under distilled water at 37 degrees C in an oven for 24 hours. Ten specimens in each group were thermocycled for 300 cycles between 5 degrees C and 55 degrees C. All the specimens were stressed to failure in an Instron Materials Testing Machine.
Results:
The results were subjected to a one-way analysis of variance (ANOVA). Statistically similar mean SBS values were grouped using the Bonferroni (Dunn) multiple comparison test. The means for the non-thermocycled group were: 26.21, 19.41, 17.69, 17.43, and 15.76. The means for the thermocycled group were: 22.90, 15.72, 14.34, 13.96 and 13.45. The differences between the means were highly significant (p < 0.0125).
Conclusions:
The shear bond strength of Variolink II and Rely XARC to IPS Empress 2 ceramic was effective. Thermocycling had a significant effect on the mean SBS values of Calibra. Thermocycling had no significant effect on the mean SBS values of the other resin cements.