Self-setting properties of a beta-dicalcium silicate reinforced calcium phosphate cement

Xiupeng Wang1, Jiandong Ye, Yingjun Wang

  • 1Key Laboratory of Specially Functional Materials and Advanced Manufacturing Technology, Ministry of Education, South China University of Technology, Guangzhou 510641, China.

Journal of Biomedical Materials Research. Part B, Applied Biomaterials
|November 2, 2006
PubMed

Keywords:
Calcium phosphate cement reinforcementInjectable bone cementBeta-dicalcium silicate applicationsBiodegradable cement materials

More Related Videos

Accessing the Cytotoxicity and Cell Response to Biomaterials09:46

Accessing the Cytotoxicity and Cell Response to Biomaterials

Published on: July 8, 2021

Sandy Soil Improvement through Microbially Induced Calcite Precipitation (MICP) by Immersion06:27

Sandy Soil Improvement through Microbially Induced Calcite Precipitation (MICP) by Immersion

Published on: September 12, 2019

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Setting Time of Cement01:12

Setting Time of Cement

The setting time of cement refers to the process of cement paste transitioning from a plastic state to a solid state. This process is crucial in construction as it dictates the timeframe for concrete placement, compaction, and finishing. The onset of this solidification is termed the initial set, indicating when the paste becomes unworkable. The final set is when the paste has solidified completely, and further handling or manipulation can no longer affect its shape. The cement strength is...
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...