Evaluation of the enamel etching capacity of six contemporary self-etching adhesives
Related Experiment Video
Updated: Jul 18, 2026
Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Geneviève Grégoire1, Yasin Ahmed
1Biomaterials Laboratory, Faculty of Odontology, University of Toulouse III, Toulouse, France. gregoire@cict.fr
Objectives:
The purpose of this study was to evaluate the capacity of six contemporary self-etch primers/adhesives to demineralize ground enamel by means of ultrastructural analysis of the etching surface under SEM and by spectroscopic measurement of the percentage of calcium and phosphate ions dissolved.
Methods:
Seventy non-carious extracted human third molars were sub-divided into 2 groups of 35 teeth each. The teeth of the first group were ground to expose flat, polished enamel surfaces 3-4mm thick. The samples thus obtained were treated with six self-etch bonding systems and a phosphoric acid gel (control group). The self-etch priming agent was then eliminated and the etched enamel surface observed by SEM. From the teeth of the second group, disc-shaped specimens were made from ground enamel and subjected to application of each of the six self-etchants. Once the etching product had been rinsed off, the rinse solution was analyzed by atomic flame spectroscopy to evaluate the percentage of calcium and phosphate ions dissolved.
Results:
SEM images show that AdheSE, Adper Prompt L-Pop and Xeno III, despite having a less intensive etching efficacy than phosphoric acid, gave a regular pattern over a considerable surface area and depth. iBond and One-Up Bond F gave less regular demineralization. For Clearfil SE Bond, the demineralization was ineffective. Results of the percentage of mineral loss show that Adper Prompt L-Pop and Xeno III were the most efficient self-etch products. AdheSE, iBond and One-Up Bond F, respectively exhibited decreasing demineralizing capacity. Clearfil SE Bond, however, gave low proportions of calcium and phosphate ions loss and was considered unsatisfactory.
Conclusion:
The action on enamel was not the same for all self-etch systems tested. The etching potential of the self-etch adhesives was lower than that of phosphoric acid but some self-etch systems, particularly those with monomers containing phosphate derivatives, gave results close to those obtained with phosphoric acid.