Determination of calcium in cement by flame-emission spectrometry with strontium as internal standard

In a flame photometer, when a solution like potassium chloride is aspirated into the flame, the solvent evaporates, leaving behind dehydrated salt. This salt dissociates into free gaseous atoms in their ground state. Some of these atoms absorb energy from the flame, leading to their excitation. The excited atoms return to the ground state, emitting photons at characteristic wavelengths. Because only electronic transitions are involved, the resulting emission lines are very narrow. The intensity...

For solutions containing mixtures of different cations, the identity of each cation can be determined by qualitative analysis. This technique involves a series of selective precipitations with different chemical reagents, each reaction producing a characteristic precipitate for a specific group of cations. Metal ions within a group are further separated by varying the pH, heating the mixture to redissolve a precipitate, or adding other reagents to form complex ions.
For instance, group IV...

Flame photometry, also known as flame emission spectrometry, is a technique used for the qualitative and quantitative analysis of elements present in a sample using a flame as the source of excitation energy. The concept of flame photometry was realized in the early 1860s by Kirchhoff and Bunsen, who discovered that specific elements emit characteristic radiation when excited in flames. The first instrument developed for this purpose was used to measure sodium (Na) in plant ash using a Bunsen...

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...