[Restoration of segmental bone defect by calcium sulfate pellet: experiment with rabbit]

To compare the effects of different calcium sulfate pellets made by different methods in treating segmental defect of bone.

Eighty New Zealand white rabbits underwent cutting off a segment in the middle part of radius so as to establish models of radial segmental defect, and than were divided into 4 groups: Group A as control group, Group B with calcium sulfate pellet made by routine method implanted into the defect, Group C with chitosan coated pressed calcium sulfate pellet implanted into the defect, and Group D with chitosan coated pressed calcium sulfate pellet combined with recombinant human bone morphogenetic protein (rhBMP)-2 implanted into the defect: X-ray photography was done every 4 weeks to observe the new bone formation. Four, 8, and 12 weeks 5 rabbits from each group were killed. The defect segments with parts of normal bone at both ends were cut off to undergo fluorescence microscopy and biomechanic three point bending test.

X-ray photography and histological examination showed that new bone formation of cortex and reconstruction of marrow cavity were seen in Groups D and C, especially in Group D. The new bone mineralization rate of Group D was significantly higher than that of Group C (P<0.05) which was significantly higher than that of Group B (P<0.01). The anti-bending strength ratio of Group D was (47.5%+/-2.1%, significantly higher than that of Group C [(39.6+/-1.7)%, F=125.3, P<0.01], and the anti-bending strength ratios of Groups D and C were both significantly higher than those of Groups B and A [(23.6+/-3.3)% and (21.3+/-2.7)%].

Chitosan coated pressed calcium sulfate pellet shows relatively higher anti-bending strength and slightly slower resorption that closely coincide with the growth rate of new bone. It can be used to restore segmental bone defect, and particularly when combined with rhBMP-2.