Osteoblast response to puerarin-loaded porous titanium surfaces: an in vitro study

Recent studies demonstrate puerarin stimulates bone formation, suggesting its potential application in dental implantology field. The aim of this study was to investigate effects of puerarin-loaded titanium surfaces on the promotion of osteogenesis in preosteoblasts (MC3T3-E1). Puerarin was prepared onto titanium surfaces with varying concentration (10(-9) M, 10(-8) M, 10(-7) M, and 10(-6) M) by biomimetic calcium phosphate deposition process. Surface characteristics were performed by field-emission scanning electron microscope (FSEM), X-ray diffractometer (XRD), and Fourier transform infrared spectroscopy (FTIR). Puerarin concentration in the coatings was performed by High-performance liquid chromatograph (HPLC) analyses. FSEM observation showed puerarin concentration influenced formation of sharp flakes in the coating. The size of flakes decreased with increase of puerarin concentrations. XRD and FTIR examinations demonstrated the puerarin concentration did not affect the chemical compositions of coatings, which composed of octacalcium phosphate (OCP). Puerarin concentration on the surfaces of 10(-8) M group was 10.22 ± 0.32 ng/cm(2) . Puerarin had an increased effect on MC3T3-E1 ALP activities. Significant differences were found in 10(-8) and 10(-7) M groups on day 4, 10(-8) , 10(-7) , and 10(-6) M groups on day 7, and 10(-8) on day 14. In Type I collagen synthesis assay, 10(-9) and 10(-8) M on day 7, 10(-8) on day 14 showed significant differences compared with control group. Furthermore, this stimulatory effect of puerarin was also observed in osteocalcin release assay (p < 0.05, at 10(-8) M and 10(-7) M, maximal at 10(-8) M). These results indicate puerarin-loaded titanium surfaces promote accelerated osteogenic differentiation of preosteoblasts, which has the potential to improve the nature of osseointegration.