Microstructure and thermal behaviour of plasma sprayed zirconia/alumina composite coating

In thermal barrier coatings (TBC), failure occurs near or at the interface between the metallic bondcoat and topcoat. On high temperature conditions, an oxide scale which is named thermally grown oxide (TGO) occurs along the bond/topcoat interface. For diminishing the creation of TGO, a dense coating with low residual stress and thermal stress buffer layer was preferable. High hardness ceramic coatings could be obtained by gas tunnel type plasma spraying, and the deposited coating had superior property in comparison with those deposited by conventional type plasma spray method. In this study, the gas tunnel type plasma spraying system was utilized to produce a zirconia/alumina functionally graded thermal barrier coating and discussed its physical and mechanical properties, thermal behavior and high temperature oxidation resistance of the coating are discussed. Consequently, the proposed system exhibited superior mechanical properties and oxidation resistance at the expenses of a slightly lower thermal insulating effect. This interlayer is preferred in order to minimize the detrimental effect of the phase transformation of gamma-Al2O3 to alpha-Al2O3.