Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs
Published on: August 8, 2022
Non-rigid calcium phosphate cement containing hydrogel microbeads and absorbable fibres seeded with umbilical cord
Wahwah TheinHan1, Michael D Weir, Carl G Simon
1Biomaterials and Tissue Engineering Division, Department of Endodontics, Prosthodontics and Operative Dentistry, University of Maryland Dental School, Baltimore, MD, USA.
Abstract:
The need for bone repair has increased as the population ages. Non-rigid calcium phosphate scaffolds could provide compliance for micro-motions within the tissues and yet have load-supporting strength. The objectives of this study were to: (a) develop a non-rigid calcium phosphate cement (CPC) with microbeads and fibre reinforcement; and (b) investigate human umbilical cord mesenchymal stem cell (hUCMSC) proliferation, osteodifferentiation and mineralization on non-rigid CPC for the first time. Non-rigid CPC was fabricated by adding extra tetracalcium phosphate in the traditional CPC and by incorporating chitosan, absorbable fibres and hydrogel microbeads. The non-rigid CPC-microbead scaffold possessed a strain-at-failure of 10.7%, much higher than the traditional CPC's strain of 0.05% which is typical for brittle bioceramics. Flexural strength of non-rigid CPC-microbead was 4-fold that of rigid CPC-microbead scaffold, while work-of-fracture (toughness) was increased by 20-fold. The strength of non-rigid CPC-microbead-fibre scaffold matched that of cancellous bone. hUCMSCs on non-rigid CPC proliferated from 100 cells/mm(2) at 1 day to 600 cells/mm(2) at 8 days. Alkaline phosphatase, osteocalcin and collagen gene expressions of hUCMSCs were greatly increased, and the cells synthesized bone minerals. hUCMSCs on non-rigid CPC-microbead-fibre constructs had higher bone markers and more mineralization than those on rigid CPC controls. In conclusion, this study developed the first non-rigid, in situ-setting calcium phosphate-microbead-fibre scaffold with a strain-at-failure exceeding 10%. hUCMSCs showed excellent proliferation, osteodifferentiation and mineralization on non-rigid CPC scaffold. The novel non-rigid CPC-hUCMSC construct with good strength, high strain-at-failure and toughness, as well as superior stem cell proliferation, osteodifferentiation and mineralization, is promising for load-bearing bone regeneration applications.