Surface-enhanced Raman scattering-active substrates of electrospun polyvinyl alcohol/gold-silver nanofibers

Surface-enhanced Raman scattering (SERS)-active substrates of polyvinyl alcohol/gold-silver (PVA/Au-Ag) nanofibers were prepared using a simple approach involving electrospinning. The tunable surface plasmon resonance (SPR) of gold-silver alloy (Au-Ag alloy) nanoparticles (NPs) was achieved by controlling the feed ratio between gold and silver precursors. A higher concentration of Au-Ag alloy NPs could be obtained than the conventional methods, using 1wt% of PVA as the stabilizer. The Au-Ag alloy structure was demonstrated by HRTEM and STEM-EDX. After the electrospinning, the Au-Ag alloy NPs were successfully embedded in PVA nanofibers, as shown in the SEM and TEM images. Raman spectra displayed an apparent enhancement in the signal of 4-mercaptobenzoic acid (4-MBA), pyridine, and thiophenol molecules pre-absorbed from their ethanol solution onto the PVA/Au-Ag nanofibers. Different SERS effects were achieved by varying the Au content or excitation wavelength.