Hydration and distance dependence of intermolecular shearing between collagen molecules in a model microfibril

In vertebrates, collagen tissues are the main component responsible for force transmission. In spite of the physiological importance of these phenomena, force transmission mechanisms are still not fully understood, especially at smaller scales, including in particular collagen molecules and fibrils. Here we investigate the mechanism of molecular sliding between collagen molecules within a fibril, by shearing a central molecule in a hexagonally packed bundle mimicking the collagen microfibril environment, using varied lateral distance between the molecules in both dry and solvated conditions. In vacuum, the central molecule slides under a stick-slip mechanism that is due to the characteristic surface profile of collagen molecules, enhanced by the breaking and reformation of H-bonds between neighboring collagen molecules. This mechanism is consistently observed for varied lateral separations between molecules. The high shearing force (>7 nN) found for the experimentally observed intermolecular distance (≈1.1 nm) suggests that in dry samples the fibril elongation mechanism relies almost exclusively on molecular stretching, which may explain the higher stiffnesses found in dry fibrils. When hydrated, the slip-stick behavior is observed only below 1.3 nm of lateral distance, whereas above 1.3 nm the molecule shears smoothly, showing that the water layer has a strong lubricating effect. Moreover, the average force required to shear is approximately the same in solvated as in dry conditions (≈2.5 nN), which suggests that the role of water at the intermolecular level includes the transfer of load between molecules.