Chlorine effect on the formation of carbon nanofibers

Platelet graphite nanofibers (GNFs) and turbostratic carbon nanofibers (CNFs) are synthesized by the thermal evaporation and decomposition of a polymer-based mixture at 700 degrees C using Ni as a catalyst. The mixture consists of poly(ethylene glycol) (PEG), serving as the carbon source, and hydrochloric acid solution (HCl(aq)), serving as the promoter/additive for the growth of CNFs. High-purity zigzag-shaped platelet GNFs form with 10 wt% HCl(aq) as an additive in the PEG. The diameters of the platelet GNFs are in the range of 40-60 nm, with lengths of a few micrometers. High-resolution transmission electron microscopy images indicate a high degree of graphitization and well ordered graphene layers along the fiber axis. In contrast, high-purity turbostratic CNFs form with 20 wt% HCl(aq) in the PEG. The diameter and length of the turbostratic CNFs are 20-40 nm and a few micrometers, respectively. The participation of HCl in the thermal process leads to the formation of Ni-Cl compounds. The amount of chlorine affects the shape of the Ni catalyst, which determines the type of CNF formed.