Experimental testing on free vibration behaviour for silicone rubbers proposed within lumbar disc prosthesis
Iuliana Rotaru1, Carmen Bujoreanu2, Adrian Bele3
1"Gheorghe Asachi" Technical University of Iasi, Faculty of Mechanical Engineering, Department of Mechanical Engineering, Mechatronics and Robotics, 61-63 Bd. Dimitrie Mangeron, 700050 Iasi, Romania; "Gr. T. Popa" University of Medicine and Pharmacy of Iasi, Faculty of Medical Bioengineering, Department of Biomedical Sciences, 9-13 M. Kogalniceanu Street, 700454 Iasi, Romania.
Abstract:
This research was focused on the damping capacity study of two types of silicone rubbers proposed as layers within total lumbar disc prostheses of ball-and-socket model. In order to investigate the damping capacity, the two silicone rubber types mainly differing by the molecular mass of polymeric matrix and the filler content, as was emphasized by scanning electron microscopy and differential scanning calorimetry, were subjected to free vibration testing. Using an adapted experimental installation, three kinds of damping testing were realised: tests without samples and tests with three samples of each type of silicone rubber (69 ShA and 99 ShA). The free vibration tests were performed at a frequency of about 6 Hz using a weight of 11.8 kg. The relative damping coefficient was determined by measuring of two successive amplitudes on the vibrogram and calculating of the logarithmic decrement. The test results with silicone rubber samples showed a relative damping coefficient of 0.058 and respectively 0.077, whilst test results without samples showed a relative damping coefficient of 0.042. These silicone rubbers were found to have acceptable damping properties to be used as layers placed inside the prosthetic components.