Related Experiment Video

Updated: Apr 8, 2026

Sputter Growth and Characterization of Metamagnetic B2-ordered FeRh Epilayers
12:20

Sputter Growth and Characterization of Metamagnetic B2-ordered FeRh Epilayers

Published on: October 5, 2013

15.2K

Controlled Anisotropic Growth of Co-Fe-P from Co-Fe-O Nanoparticles

Adriana Mendoza-Garcia1, Huiyuan Zhu1,2, Yongsheng Yu1,3

  • 1Department of Chemistry, Brown University, Providence, RI 02912 (USA).

Angewandte Chemie (International Ed. in English)
|June 30, 2015
PubMed

Keywords:
cobalt-iron phosphidesmetal oxide phosphidationnanorodsoxygen evolution reaction

More Related Videos

Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production08:40

Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production

Published on: December 6, 2021

4.4K
Ligand-Mediated Nucleation and Growth of Palladium Metal Nanoparticles11:54

Ligand-Mediated Nucleation and Growth of Palladium Metal Nanoparticles

Published on: June 25, 2018

10.9K

Related Concept Videos

Precipitate Formation and Particle Size Control01:16

Precipitate Formation and Particle Size Control

In precipitation gravimetry, the precipitating agent should react specifically or selectively with the analyte. While a specific reagent reacts with the analyte alone, a selective reagent can react with a limited number of chemical species.
The obtained precipitate should be either a pure substance of known composition or easily converted to one by a simple process, such as ignition or drying. In addition, the precipitate should be insoluble and easily filterable. In general, filterability...
7.2K
Colloidal precipitates01:09

Colloidal precipitates

The high insolubility of some precipitates can result in an unfavorable relative supersaturation. This can lead to colloidal particles with a large surface-to-mass ratio, where adsorption is promoted. For instance, in the precipitation of silver chloride, silver ions are adsorbed on the surface of the colloidal particles, forming a primary layer. This layer attracts ions of opposite charge (such as nitrate ions), forming a diffuse secondary layer of adsorbed ions. This electric double layer...
6.9K
Ferromagnetism01:31

Ferromagnetism

Materials like iron, nickel, and cobalt consist of magnetic domains, within which the magnetic dipoles are arranged parallel to each other. The magnetic dipoles are rigidly aligned in the same direction within a domain by quantum mechanical coupling among the atoms. This coupling is so strong that even thermal agitation at room temperature cannot break it. The result is that each domain has a net dipole moment. However, some materials have weaker coupling, and are ferromagnetic at lower...
3.6K
Anionic Chain-Growth Polymerization: Mechanism01:04

Anionic Chain-Growth Polymerization: Mechanism

The mechanism for anionic chain-growth polymerization involves initiation, propagation, and termination steps. In the initiation step, a nucleophilic anion, such as butyl lithium, initiates the polymerization process by attacking the π bond of the vinylic monomer. As a result, a carbanion, stabilized by the electron‐withdrawing group, is generated. The resulting carbanion acts as a Michael donor in the propagation step and attacks the second vinylic monomer, which acts as a Michael...
2.6K
Pinching-off of Coated Vesicles01:32

Pinching-off of Coated Vesicles

Vesicle budding is orchestrated by distinct cytosolic proteins such as adaptor proteins, coat proteins, and GTPases. To initiate vesicle budding, membrane-bending proteins containing crescent-shaped BAR domains bind to the lipid heads in the bilayer and distort the membrane to form a protein-coated vesicle bud. Adaptors proteins such as AP2 for clathrin-coated vesicles can nucleate on the deformed membrane. Finally, coat proteins such as clathrin or COPI and COPII assemble into a coat forming...
4.4K
Imperfections in Crystal Structure: Non-Stoichiometric Defects01:29

Imperfections in Crystal Structure: Non-Stoichiometric Defects

Non-stoichiometric defects refer to a type of defect in the crystal structure of a compound where the ratio of its constituent elements deviates from the ideal stoichiometric ratio. There are two main types of non-stoichiometric defects: metal excess defects and metal deficiency defects.Metal excess defects occur when there is a slight surplus of metal ions than what is required by the stoichiometric ratio of the compound. For example, heating a sodium chloride crystal in sodium vapor results...
82