Nucleation of Ga droplets on Si and SiOx surfaces

We report on gallium droplet nucleation on silicon (100) substrates with and without the presence of the native oxide. The gallium deposition is carried out under ultra-high vacuum conditions at temperatures between 580 and 630 °C. The total droplet volume, obtained from a fit to the diameter-density relation, is used for sample analysis on clean silicon surfaces. Through a variation of the 2D equivalent Ga thickness, the droplet diameter was found to be between 250-1000 nm. Longer annealing times resulted in a decrease of the total droplet volume. Substrate temperatures of 630 °C and above led to Ga etching into the Si substrates and caused Si precipitation around the droplets. In contrast, we obtained an almost constant diameter distribution around 75 nm over a density range of more than two orders of magnitude in the presence of a native oxide layer. Furthermore, the droplet nucleation was found to correlate with the density of surface features on the 'epi-ready' wafer.