Microwave-assisted Bi₂Se₃ nanoparticles using various organic solvents

Microwave assisted Bi2Se3 nanoparticles were synthesized from five different solvents DMF, EG, EG+H2O, EDA+dil.HNO3 and N2H4+H2O+Ethanol. The influence of solvents on purity of the compound was analysed by using X-ray diffraction patterns. The result indicates pure rhombohedral Bi2Se3 nanoparticles formed for N2H4+H2O+Ethanol. The presence of vibrational bands in the range of 400-800 cm(-1) is confirmed the formation of Bi2Se3. The maximum optical absorption observed around 450 nm and the band gap values are found in the range of 1.5 eV-2.17 eV for all the solvents. The nanostructure of the Bi2Se3 particles change with solvents. From the experimental results, the solvent N2H4+H2O+Ethanol produces pure nanosize Bi2Se3 particles under the microwave assisted method.