Hydrostatic Extrusion and Nano-Hardness of Nanocrystalline Grade 2 Titanium

The structure and corrosion resistance of Grade 2 titanium subjected to the hydroextrusion processes were examined. The microstructure was characterized using optical microscopy and transmission electron microscopy. The corrosion resistance was determined using the impedance and potentiodynamic methods, in 0.1 M H2SO4 solutions and an acidified 0.1 M NaCl solution with a pH of 4.2, at ambient temperature. Nanohardness tests were performed under a load of 100 mN. It has been demonstrated that the hydroextrusion method makes it possible to obtain relatively homogeneous nanocrystalline titanium Grade 2 with an increased hardness, the elastic modulus almost unchanged with respect to that of the initial structure and a lower corrosion resistance.