A Comprehensive Study on Mo/CdTe Metal-Semiconductor Interface Deposited by Radio Frequency Magnetron Sputtering

Metal-semiconductor (MS) junction between Mo and CdTe, which is one of the fundamental issues for CdTe based solar cell, has been investigated for films deposited on different substrates. XRD pattern of Mo/CdTe films on the polyimide (PI) substrate shows a strong preferential orientation of MoTe2 in (100) at 2θ = 29.44 degrees, which becomes less apparent as deposition time of CdTe increases. However, on soda lime glass (SLG) no such XRD reflection pattern is observed. Moreover, from EDX measurement, Mo-Te compound also identifies MoTe2 at Mo/CdTe interface on PI substrate, which is not present on SLG. Bulk carrier concentration of Mo/CdTe films on PI substrate for lower deposition time of CdTe is found 1.42 x 10(18) cm(-3), which is almost equal to MoTe2. Thereafter, it decreases as CdTe growth time increases. The type of unintentionally formed MoTe2 on PI substrate is found to be n-type in nature. Lattice constants of a = 6.5 Å for CdTe and a = 3.52 Å for MoTe2 are found from nanostructure study by TEM.