High-Pressure Raman and Calorimetry Studies of Vanadium(III) Alkyl Hydrides for Kubas-Type Hydrogen Storage

Reversible hydrogen storage under ambient conditions has been identified as a major bottleneck in enabling a future hydrogen economy. Herein, we report an amorphous vanadium(III) alkyl hydride gel that binds hydrogen through the Kubas interaction. The material possesses a gravimetric adsorption capacity of 5.42 wt % H2 at 120 bar and 298 K reversibly at saturation with no loss of capacity after ten cycles. This corresponds to a volumetric capacity of 75.4 kgH2  m(-3) . Raman experiments at 100 bar confirm that Kubas binding is involved in the adsorption mechanism. The material possesses an enthalpy of H2 adsorption of +0.52 kJ mol(-1) H2 , as measured directly by calorimetry, and this is practical for use in a vehicles without a complex heat management system.