Composites of fluoroapatite and methylmethacrylate-based polymers (PMMA) for biomimetic tooth replacement

Synthetic composite materials that mimic the structure and composition of mammalian tooth enamel were prepared by mixing fluoroapatite rods (diameter 2-3 μm, thickness about 0.5 μm) and methylmethacrylate (MMA), followed by polymerization either during or immediately after ultracentrifugation, using either a tertiary amine/radical initiator for polymerization at room temperature or a radical initiator for thermal polymerization. This led to mineral-rich composites (mineral content between 50 and 75 wt%). To enhance the mechanical stability and the interaction between fluoroapatite and polymer matrix, small amounts of differently functionalized MMA monomers were added to the co-monomer mixture. Another approach was the coating of the fluoroapatite rods with silica and the polymerization in the presence of a siloxane-functionalized MMA monomer. The hardness of the composites was about 0.2-0.4 GPa as determined by Vickers indentation tests, about 2 times higher than the polymer matrix alone. The composites had a good resistance against acids (60 min at pH 3, 37 °C).