Synthesis and characterization of a material derived from 4-mercaptobenzoic acid: A novel platform for...

This paper reports the electrochemical modification of pencil carbon graphite electrodes with a polymeric material derived from 4-mercaptobenzoic acid. Acidic solutions (pH 0 and 5.02) yielded an insulating polymeric film with anionic permselective properties. Scanning Electron Microscopy (SEM) analysis showed a complete coverage of the carbon graphite electrodes with a laminar-like polymeric structure. Different characterization studies indicate that the carboxyl group remained unchanged since the absorbance peak and oxidation potential did not change with the increase in pH at the pK_a accounting for the carboxyl/carboxylate redox transition. The functionalized matrix was activated using carbodiimide, succinimide and an amine-modified oligonucleotide. The immobilization and hybridization processes were successfully verified using the redox electroactive indicator methylene blue, where better electrochemical signals were obtained when compared with the traditional self-assembled monolayer system. The selectivity of the system was verified using a noncomplementary target where no significant difference in electric current was observed when compared to the system containing only the probe. The method showed a good linear correlation coefficient (r²=0.9915), low limit of detection (1.17nmolL^-1), and an acceptable precision (RSD=2.75%). The proposed method is suitable for further studies using different sequences of oligonucleotides.