Far-UV Annealed Inkjet-Printed In₂O₃ Semiconductor Layers for Thin-Film Transistors on a Flexible Polyethylene...

The inkjet-printing process of precursor solutions containing In nitrate dissolved in 2-methoxyethanol is optimized using ethylene glycol as a cosolvent that allows the stabilization of the droplet formation, leading to a robust, repeatable printing process. The inkjet-printed precursor films are then converted to In₂O₃ semiconductors at flexible-substrate-compatible low temperatures (150-200 °C) using combined far-ultraviolet (FUV) exposure at ∼160 nm and thermal treatment. The compositional nature of the precursor-to-metal oxide conversion is studied using grazing incidence X-ray diffraction (GIXRD), X-ray reflectivity (XRR), and Fourier transform infrared (FTIR) spectroscopy that indicate that amorphous, high density (up to 5.87 g/cm³), and low impurity In₂O₃ films can be obtained using the combined annealing technique. Prolonged annealing (180 min) at 150 °C yields enhancement-mode TFTs with saturation mobility of 4.3 cm²/(Vs) and ∼1 cm²/(Vs) on rigid Si/SiO₂ and flexible plastic PEN substrates, respectively. This paves the way for manufacturing relatively high-performance, printed metal-oxide TFT arrays on cheap, flexible substrate for commercial applications.