Efficient Semipolar (11-22) 550 nm Yellow/Green InGaN Light-Emitting Diodes on Low Defect Density (11-22)
Hongjian Li1, Michel Khoury1, Bastien Bonef1
1Materials Department, University of California , Santa Barbara, California 93106, United States.
Abstract:
We demonstrate efficient semipolar (11-22) 550 nm yellow/green InGaN light-emitting diodes (LEDs) with In0.03Ga0.97N barriers on low defect density (11-22) GaN/patterned sapphire templates. The In0.03Ga0.97N barriers were clearly identified, and no InGaN clusters were observed by atom probe tomography measurements. The semipolar (11-22) 550 nm InGaN LEDs (0.1 mm2 size) show an output power of 2.4 mW at 100 mA and a peak external quantum efficiency of 1.3% with a low efficiency drop. In addition, the LEDs exhibit a small blue-shift of only 11 nm as injection current increases from 5 to 100 mA. These results suggest the potential to produce high efficiency semipolar InGaN LEDs with long emission wavelength on large-area sapphire substrates with economical feasibility.
More Related Videos
10:41Enhanced Electron Injection and Exciton Confinement for Pure Blue Quantum-Dot Light-Emitting Diodes by Introducing Partially Oxidized Aluminum Cathode
Published on: May 31, 2018
07:44Production and Characterization of Vacuum Deposited Organic Light Emitting Diodes
Published on: November 16, 2018