Electrospun carboxyl multi-walled carbon nanotubes grafted polyhydroxybutyrate composite nanofibers membrane
Cai Zhijiang1, Zhu Cong2, Guo Jie2
1School of Textiles, Tianjin Polytechnic University, No 399 BingShuiXi Street, XiQing District, Tianjin 300387, China; State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, No 399 BingShuiXi Street, XiQing District, Tianjin 300387, China.
Abstract:
Electrospun polyhydroxybutyrate (PHB)/carboxyl multi-walled carbon nanotubes grafted polyhydroxybutyrate (CMWCNT-g-PHB) composite nanofibers scaffolds were fabricated by electrospinning technology. The grafted product CMWCNT-g-PHB was prepared by condensation reactions between the carboxyl groups of CMWCNT and hydroxyl groups of PHB molecules and characterized by FTIR, XRD, XPS, TG and TEM measurements. The surface morphology, hydrophilicity and tensile mechanical properties of the electrospun PHB/CMWCNT-g-PHB composite nanofibers membrane scaffolds were investigated. The values of tensile strength, breaking elongation rate, initial modulus and fracture energy of the composite nanofibers scaffolds can reach to 4.64MPa, 255.59%, 88MPa and 109.73kJ/m2, respectively. The biodegradability and cytocompatibility of the electrospun composite nanofibers scaffolds were preliminarily evaluated. The as-prepared electrospun PHB/CMWCNT-g-PHB composite nanofibers scaffolds with the characteristics of large specific area, high porosity, good biodegradability and cytocompatibility as well as sufficient mechanical properties should be more promising in the field of tissue engineering scaffolds and biological medicine.