Three Dimensional Nitrogen-Doped and Nitrogen, Sulfur-Codoped Graphene Hydrogels for Electrode Materials in...

In present work, reduced graphene oxide hydrogels (RGOHs) with three-dimensional (3D) porous structure are prepared through chemical reduction method by using aminourea (NRGOHs) and aminothiourea (NSRGOHs) as reductants. The as-prepared RGOHs are considered not only as promising electrode materials for supercapacitors, but also the doping of nitrogen (aminourea, NRGOHs) or nitrogen/sulfur (aminothiourea, NSRGOHs) can improve electrochemical performance through faradaic pseudocapacitance. The optimized samples have been prepared by controlling the mass ratios of graphene oxide (GO) to aminourea or aminothiourea to be 1:1, 1:2 and 1:5, respectively. With adding different amounts of aminourea or aminothiourea, the obtained RGOHs exhibited different electrochemical performance in supercapacitors. With increasing the dosage of the reductants, the RGOHs revealed better specific capacitances. Moreover, NSRGOHs with nitrogen, sulfur-codoping exhibited better capacitance performance than that of NRGOHs with only nitrogen-doping. NSRGOHs showed excellent capacitive performance with a very high specific capacitance up to 232.2, 323.3 and 345.6 F g-1 at 0.2 A g-1, while NRGOHs showed capacitive performance with specific capacitance up to 220.6, 306.5 and 332.7 F g-1 at 0.2 A g-1. This provides a strategy to improve the capacitive properties of RGOHs significantly by controlling different doping the materials.