Enhancement of Inverted Polymer Solar Cells Performances Using Cetyltrimethylammonium-Bromide Modified ZnO

In this study, the performance and stability of inverted bulk heterojunction (BHJ) polymer solar cells (PSCs) is enhanced by doping zinc oxide (ZnO) with 0-6 wt % cetyltrimethylammonium bromide (CTAB) in the sol-gel ZnO precursor solution. The power conversion efficiency (PCE) of the optimized 3 wt % CTAB-doped ZnO PSCs was increased by 9.07%, compared to a PCE of 7.31% for the pristine ZnO device. The 0-6 wt % CTAB-doped ZnO surface roughness was reduced from 2.6 to 1 nm and the number of surface defects decreased. The X-ray photoelectron spectroscopy binding energies of Zn 2p^3/2 (1021.92 eV) and 2p^1/2 (1044.99 eV) shifted to 1022.83 and 1045.88 eV, respectively, which is related to strong chemical bonding via bromide ions (Br^-) that occupy oxygen vacancies in the ZnO lattice, improving the PCE of PSCs. The concentration of CTAB in ZnO significantly affected the work function of PSC devices; however, excessive CTAB increased the work function of the ZnO layer, resulting from the aggregation of CTAB molecules. In addition, after a 120-hour stability test in the atmosphere with 40% relative humidity, the inverted device based on CTAB-doped ZnO retained 92% of its original PCE and that based on pristine ZnO retained 68% of its original PCE. The obtained results demonstrate that the addition of CTAB into ZnO can dramatically influence the optical, electrical, and morphological properties of ZnO, enhancing the performance and stability of BHJ PSCs.