Welding strength of NiTi wires
Tatyane Ribeiro Mesquita1, Lídia Parsekian Martins1, Renato Parsekian Martins1
1Universidade Estadual Paulista, Faculdade de Odontologia de Araraquara, Departamento de Clínica Infantil (Araraquara/SP, Brazil).
Objective:
To identify the appropriate power level for electric welding of three commercial brands of nickel-titanium (NiTi) wires.
Methods:
Ninety pairs of 0.018-in and 0.017 × 0.025-in NiTi wires were divided into three groups according to their manufacturers - GI (Orthometric, Marília, Brazil), GII (3M OralCare, St. Paul, CA) and GIII (GAC,York, PA) - and welded by electrical resistance. Each group was divided into subgroups of 5 pairs of wires, in which welding was done with different power levels. In GI and GII, power levels of 2.5, 3, 3.5, 4, 4.5 and 5 were used, while in GIII 2.5, 3, 3.5 and 4 were used (each unit of power of the welding machine representing 500W). The pairs of welded wires underwent a tensile strength test on an universal testing machine until rupture and the maximum forces were recorded. Analysis of variance (ANOVA) and post-hoc tests were conducted to determine which subgroup within each brand group had the greatest resistance to rupture.
Results:
The 2.5 power exhibited the lowest resistance to rupture in all groups (43.75N for GI, 28.41N for GII and 47.57N for GIII) while the 4.0 power provided the highest resistance in GI and GII (97.90N and 99.61N, respectively), while in GIII (79.28N) the highest resistance was achieved with a 3.5 power welding.
Conclusions:
The most appropriate power for welding varied for each brand, being 4.0 for Orthometric and 3M, and 3.5 for GAC NiTi wires.
Related Concept Videos
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:30Relation Between Tensile Strength and Compressive Strength of Concrete
02:18The Equilibrium Binding Constant and Binding Strength
01:18Magnetic Field Due to Two Straight Wires
01:13Household Wiring And Electrical Safety