Fabrication and characterization of polycaprolactone and tricalcium phosphate composites for tissue engineering...

β-Tricalcium phosphate (β-TCP) is an osteoconductive material which has been used for clinical purposes for several years, as is polycaprolactone (PCL), which has already been approved for a number of medical and drug delivery devices. In this study we have incorporated various concentrations of β-TCP into PCL with the aim of developing an injectable, mechanically strong, and biodegradable material which can be used for medical purposes without organic solvents.

This study assesses the physical and chemical properties of this material, evaluates the in vitro bioactivity of the PCL/β-TCP composites, and analyzes cell proliferation and osteogenic differentiation when using human bone marrow mesenchymal stem cells (hBMSCs).

The results show that weight losses of approximately 5.3%, 12.1%, 18.6%, and 25.2%, were observed for the TCP0, TCP10, TCP30, and TCP50 composites after immersion in simulated body fluid for 12 weeks, respectively, indicating significant differences (P < 0.05). In addition, PCL/β-TCP composites tend to have lower contact angles (47 ± 1.5° and 58 ± 1.7° for TCP50 and TCP30, respectively) than pure PCL (85 ± 1.3°), which are generally more hydrophilic. After 7 days, a significant (22% and 34%, respectively) increase (P < 0.05) in alkaline phosphatase level was measured for TCP30 and TCP50 in comparison with the pure PCL.

PCL/TCP is biocompatible with hBMSCs. It not only promotes proliferation of hBMSCs but also helps to differentiate reparative hard tissue. We suggest 50% (weight) PCL-containing β-TCP biocomposites as the best choice for hard tissue repair applications.