Enhanced Poly(Propylene Carbonate) with Thermoplastic Networks: A One-Pot Synthesis from Carbon Dioxide, Propylene...

Thermally and mechanically enhanced poly(propylene carbonate) (PPC) with networks was prepared by adding a cyclic carboxylic dianhydride, bicyclo(2,2,2)oct-7-ene-2,3,5,6-tetracarboxylic dianhydride (BTCDA), in the CO₂/propylene oxide (PO) copolymerization. The obtained copolymers were characterized by FT-IR, ¹H NMR, DSC, and TGA. The gel, melt flow rate, hot-set elongation, and tensile properties were also measured. The formation of networks was confirmed by the presence of gel and the shape recovery after the hot-set elongation test. The minimum permanent deformation of the copolymer is 3.8% and that of PPC is 4539% higher than this value. The results show that BTCDA units are inserted into the backbone of PPC, and the PPC chains are connected successfully owing to cyclic multifunctional anhydride groups in BTCDA. With increasing feed molar ratio of BTCDA to PO from 1 to 4%, the yield strength of copolymers increases from 18.1 to 37.4 MPa compared to 12.9 MPa of PPC. The 5% weight-loss degradation temperatures and maximum weight-loss degradation temperatures greatly increase up to 276.4 and 294.7 °C, respectively, which are 58.6 °C and 55.1 °C higher than those of PPC. These enhanced properties originate from the formation of crosslinks by the rigid and bulky multifunctional dianhydride.