Effects of 10-MDP Based Primer on Shear Bond Strength between Zirconia and New Experimental Resin Cement

To date, numerous materials in the dental field are marketed to ensure stable adhesive cementation of zirconia ceramics (Y-TZP). The aims of this study were to assess the shear bond strength of the new experimental cement Surgi Dual Flo' Zr to Y-TZP compared to Panavia V5 cement, and to evaluate the effect of 10-MDP (10-methacryloyloxydecyl dihydrogen phosphate) containing primer on their bond strength. Twenty composite cylinders and Y-TZP disks were adhesively luted and divided into four groups based on cement type used and application or not of 10-MDP. The groups (n = 5 each) were S 10MDP (Surgi Dual Flo' Zr with 10-MDP); S no 10MDP (Surgi Dual Flo' Zr without 10-MDP); P 10MDP (Panavia V5 with 10-MDP); P no 10MDP (Panavia V5 without 10-MDP). Maximum load resistance (ML) and shear bond strength (SBS) were tested and mode of failure qualitative documented via scanning electron microscopy. The data were analyzed with one-way ANOVA, Holm-Sidak method, and Bayesian analysis. ML and SBS were significantly higher in S 10MDP than in S no 10MDP; and in P 10MDP than in P no 10MDP (p < 0.05). No significant differences were found between S 10MDP and P 10MDP; S no 10MDP and P no 10MDP (p > 0.05). Cohesive, adhesive, and mixed failure occurred among the groups. Bond strength between the experimental resin-based cement and Y-TZP was adequate for clinical application when 10-MDP was added. 10-MDP containing primer was effective improving the bond strength to Y-TZP more than the different type of resinous cement.