Nanoengineering 2D Dendritic PdAgPt Nanoalloys with Edge-Enriched Active Sites for Enhanced Alcohol Electroxidation...

Lots of research studies reveal that the surface atoms on the top/bottom facets of the nanosheets are the key features in enhancing electrocatalytic activity while the edge and corner sites of electrocatalysts often possess superior activity. Herein, we report 2D dendritic PdAgPt ternary nanoalloys with abundant crystal defects such as steps, twin boundary, and atomic holes, which can effectively work as catalytic active-sites. The morphology of PdAgPt nanoalloys can be regulated readily from dendritic nanosheets to nanowheels. Compared with binary Pd₆₈Ag₃₂ nanodendrites, Pd₆₂Pt₃₈ nanospheres, and Pt/C catalyst, the composition- and morphology-optimized Pd₄₃Ag₂₁Pt₃₆ nanowheels exhibit the best mass/specific activity and stability for methanol/ethanol oxidation reaction (MOR/EOR). The mass peak current density for EOR/MOR of Pd₄₃Ag₂₁Pt₃₆ is 7.08/3.50 times of the Pt/C catalyst. Simultaneously, the hydrogen evolution reaction performance of the Pd₄₃Ag₂₁Pt₃₆ nanowheels in terms of the lowest overpotential of 9 mv at a current density of 10 mA/cm² and high electrochemical stability is much better than that of binary Pd₆₈Ag₃₂ nanodendrites, Pd₆₂Pt₃₈ nanospheres, and Pt/C.