Fabrication of Molybdenum Oxide/Activated Carbon Using Liquid Phase Plasma Reaction and Its Electrochemical
Sang-Chai Kim1, Young-Kwon Park2, Hangun Kim3
1Department of Environmental Education, Mokpo National University, Muan 58554, Korea.
Abstract:
In this study, molybdenum oxide/carbon nanocomposites (MOCNCs) were prepared by precipitating molybdenum oxide nanoparticles on activated carbon powder using liquid phase plasma process. The molybdenum oxide nanoparticles were impregnated on the AC surface and the amount impregnated was dependent on the concentration of the molybdenum precursor. MoO₃ nanoparticles were predominantly precipitated and their size was about 20-80 nm. The specific capacitance of MOCNCs was increased with increasing the amount of molybdenum nanoparticles. Moreover, the resistances of MOCNCs were reduced than that of bare AC.