Synthesis and properties of porous piezoelectric BT/PHBV composite scaffold
Hua Jiao1, Sen Song1, Kang Zhao1
1School of Materials Science and Engineering, Xi'an University of Technology, Xi'an, China.
Abstract:
The biodegradable material poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) scaffold has good biodegradability, but poor biocompatibility limits its application in the biological field. And it can effectively improve its biological activity by compounding with the bone conduction activity material of Barium titanate (BT). The PHBV and piezoelectric material BT were prepared into porous composite scaffolds with porosity of 45-50%. The mechanical properties and electrical properties of BT/PHBV scaffolds were systematically studied. The results showed that the piezoelectric coefficient d was 0.2-1.5 pC/N. Moreover, the compressive strength and elastic modulus were 1.0-2.0 MPa and 100-200 MPa, respectively. The results of degradation and mineralization showed that BT/PHBV scaffolds had good degradation and mineralization performance which was indicated that the materials had good biological activity.