Theoretical Calculation and Experimental Verification for Dislocation Reduction in Germanium Epitaxial Layers with
Motoki Yako1, Yasuhiko Ishikawa2, Eiji Abe1
1Department of Materials Engineering, The University of Tokyo.
Abstract:
Reduction of threading dislocation density (TDD) in epitaxial germanium (Ge) on silicon (Si) has been one of the most important challenges for the realization of monolithically integrated photonics circuits. The present paper describes methods of theoretical calculation and experimental verification of a novel model for the reduction of TDD. The method of theoretical calculation describes the bending of threading dislocations (TDs) based on the interaction of TDs and non-planar growth surfaces of selective epitaxial growth (SEG) in terms of dislocation image force. The calculation reveals that the presence of voids on SiO2 masks help to reduce TDD. Experimental verification is described by germanium (Ge) SEG, using an ultra-high vacuum chemical vapor deposition method and TD observations of the grown Ge via etching and cross-sectional transmission electron microscope (TEM). It is strongly suggested that the TDD reduction would be due to the presence of semicylindrical voids over the SiO2 SEG masks and growth temperature. For experimental verification, epitaxial Ge layers with semicylindrical voids are formed as the result of SEG of Ge layers and their coalescence. The experimentally obtained TDDs reproduce the calculated TDDs based on the theoretical model. Cross-sectional TEM observations reveal that both the termination and generation of TDs occur at semicylindrical voids. Plan-view TEM observations reveal a unique behavior of TDs in Ge with semicylindrical voids (i.e., TDs are bent to be parallel to the SEG masks and the Si substrate).
Related Concept Videos
01:12Fermi Level Dynamics
Electron affinity in semiconductors refers to the energy gap between the minimum of its conduction band and the vacuum level and it is a critical parameter in determining how easily a semiconductor can accept additional electrons.
The work...
01:27Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
01:24Metal-Semiconductor Junctions
Schottky Barriers
Schottky barriers arise when a metal with a work function (Φm) contacts a semiconductor with a different work function (Φs). Initially, electrons transfer until the Fermi levels of the metal and semiconductor align at equilibrium. For instance, if Φm > Φs, the semiconductor Fermi level is higher than the metal's before contact. The...