[Evaluation of microtensile bond strength between resin composite and glass ceramic]

To evaluate the microtensile bond strength of resin composite to glass ceramic, and the effect of surface treatment of resin composite and thermal cycling aging on the microtensile bond strength.

Rectangular blocks were made with dentin of extracted molars, resin composite or feldspathic glass ceramic respectively. The bonding surfaces of these rectangular blocks were sanded by 600-grit silicon carbide paper before luting. A self-etching resin cement was used as luting agent. The specimens were divided into groups according to the types of substrates of adhesion (dentin/glass ceramic or resin composite/glass ceramic), the way of surface treatments and whether thermal cycling aging ocurred. The dentin blocks were adhered to ceramic blocks as controls (group A1 and A2). The resin composite blocks were adhered to the ceramic blocks as experiment groups. The resin composite surfaces were treated by different ways before luting: no extra surface treatment (group B1 and B2), treated by ethyl methacrylate solution (group C1 and C2) or silane coupling agent (group D1 and D2), coarsened by 360-grit silicon carbide paper (group E1 and E2) or polished by 1 200-grit silicon carbide paper (group F1 and F2). After luting, the microtensile bond strength of the specimens were tested before (group A1-F1) or after (group A2-F2) thermal cycling aging. After microtensile bond strength test, the fracture bonding surfaces of the specimens were observed by a scanning electron microscopy to determine the type of bonding failure. The data were statistically analyzed using one-way analysis of variance.

The microtensile bond strength of resin composite to glass ceramic with no extra treatment achieved high bond values before and after thermal cycling [B1 (30.02±3.85) MPa, B2 (26.83±3.14) MPa], which were statistically different from those of the control groups [A1 (20.55±4.51) MPa, A2 (12.94±0.69) MPa, P < 0.05]. The microtensile bond strength between the glass ceramic and resin composite did not increase after different surface treatments of resin composite.

The microtensile bond strength between resin composite and glass ceramic achieved as similar bond strength as that between dentin and glass ceramic and even better. Surface treatment of resin composite via methyl methacrylate solution, silane coupling agent, coarsening, or polishing did not increase the microtensile bond strength effectually.