Pullout strength of pedicle screws using cadaveric vertebrae with or without artificial demineralization

To evaluate the differences in the pullout strength and displacement of pedicle screws in cadaveric thoracolumbar vertebrae with or without artificial demineralization.

Five human lumbar and five thoracic vertebrae from one cadaver were divided into two hemivertebrae. The left-side specimens were included in the simulated osteopenic model group and the right-side bones in a control group. In the model group, we immersed each specimen in HCl (1 N) solution for 40 minutes. We measured bone mineral density (BMD) using dual-energy X-ray absorptiometry and quantitative computerized tomography. We inserted polyaxial pedicle screws into the 20 pedicles of the cadaveric lumbar and thoracic spine after measuring the BMD of the 2 hemivertebrae of each specimen. We measured the pullout strength and displacement of the screws before failure in each specimen using an Instron system.

The average pullout strength of the simulated osteopenic model group was 76% that of the control group. In the control and model groups, the pullout strength was 1678.87±358.96 N and 1283.83±341.97 N, respectively, and the displacement was 2.07±0.34 mm and 2.65±0.50 mm, respectively (p<.05). We detected positive correlations between pullout strength and BMD in the control group and observed a negative correlation between displacement and BMD in the model group.

By providing an anatomically symmetric counterpart, the human cadaveric model with or without demineralization can be used as a test bed for pullout tests of the spine. In the simulated osteopenic model group, pullout strength was significantly decreased compared with the untreated control group.

Decreased bone mineral density may significantly reduce the pullout strength of a pedicle screw, even though the range is osteopenic rather than osoteoporotic.