Reversing the Humidity Response of MoS₂- and WS₂-Based Sensors Using Transition-Metal Salts

Two-dimensional materials, such as transition-metal dichalcogenides (TMDs), are attractive candidates for sensing applications due to their high surface-to-volume ratio, chemically active edges, and good electrical properties. However, their electrical response to humidity is still under debate and experimental reports remain inconclusive. For instance, in different studies, the impedance of MoS₂-based sensors has been found to either decrease or increase with increasing humidity, compromising the use of MoS₂ for humidity sensing. In this work, we focus on understanding the interaction between water and TMDs. We fabricated and studied humidity sensors based on MoS₂ and WS₂ coated with copper chloride and silver nitrate. The devices exhibited high chemical stability and excellent humidity sensing performance in relative humidity between 4 and 80%, with response and recovery times of 2 and 40 s, respectively. We have systematically investigated the humidity response of the materials as a function of the type and amount of induced metal salt and observed the reverse action of sensing mechanisms. This phenomenon is explained based on a detailed structural analysis of the samples considering the Grotthuss mechanism in the presence of charge trapping, which was represented by an appropriate lumped-element model. Our findings open up a possibility to tune the electrical response in a facile manner and without compromising the high performance of the sensor. They offer an insight into the time-dependent performance and aging of the TMD-based sensing devices.