The pH and Bismuth Oxide Particle Size can Affect Diametral Tensile Strength of Mineral Trioxide Aggregate

Mohammad Ali Saghiri1, Armen Asatourian2, Behnam Rahmani3

  • 1Director of Biomaterial and Prosthodontic Laboratory, Department of Restorative Dentistry, Rutgers School of Dental Medicine, NJ; Department of Endodontics, University of the Pacific, Arthur A. Dugoni School of Dentistry, San Francisco, California, USA.

European Endodontic Journal
|May 28, 2021
PubMed
Abstract

More Related Videos

Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles07:47

Reverse Microemulsion-mediated Synthesis of Monometallic and Bimetallic Early Transition Metal Carbide and Nitride Nanoparticles

Published on: November 27, 2015

11.1K
Facile Preparation of Ultrafine Aluminum Hydroxide Particles with or without Mesoporous MCM-41 in Ambient Environments05:50

Facile Preparation of Ultrafine Aluminum Hydroxide Particles with or without Mesoporous MCM-41 in Ambient Environments

Published on: May 11, 2017

11.0K

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
293
Unsoundness of Aggregate due to Volume Change01:26

Unsoundness of Aggregate due to Volume Change

Unsoundness in aggregates due to volume changes is primarily caused by the physical alterations aggregates undergo, such as freezing and thawing, thermal changes, and wetting and drying. Unsound aggregates, when subjected to these changes, result in volume change upon disintegration. This, in turn, contributes to the deterioration of concrete, including scaling, pop-outs, and cracking. Particular types of aggregates, such as porous flints, cherts, and those containing clay minerals, are...
244
Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in...
398
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen...
262
Relation Between Tensile Strength and Compressive Strength of Concrete01:30

Relation Between Tensile Strength and Compressive Strength of Concrete

Concrete is a fundamental building material, and understanding its strengths is crucial for construction projects. The relationship between its tensile and compressive strengths is intricate, showing that while these strengths are related, they do not increase at the same rate. Tensile strength's growth is slower and is affected by various factors such as the methods used for testing, the size and shape of the specimen, the texture of the aggregate used, and the moisture content of the...
413
Maximum Size of Aggregate01:12

Maximum Size of Aggregate

The maximum size of aggregate is defined as the aperture of the sieve retaining 15 percent or more of the particles present in the aggregate sample. The aggregate's maximum size impacts the concrete's water requirement, workability, and strength. Larger aggregates reduce the surface area needing cement paste coverage, which can lower water needs, thereby allowing a decrease in the water-to-cement ratio when the desired workability and richness of the mix are to be maintained, which can...
303