Effect of the Synthetic Method on the Properties of Ni-Based Hydrogen Oxidation Catalysts

The latest progress in alkaline anion-exchange membranes has led to the expectation that less costly catalysts than those of the platinum-group metals may be used in anion-exchange membrane fuel cell devices. In this work, we compare structural properties and the catalytic activity for the hydrogen-oxidation reaction (HOR) for carbon-supported nanoparticles of Ni, Ni₃Co, Ni₃Cu, and Ni₃Fe, synthesized by chemical and solvothermal reduction of metal precursors. The catalysts are well dispersed on the carbon support, with particle diameter in the order of 10 nm, and covered by a layer of oxides and hydroxides. The activity for the HOR was assessed by voltammetry in hydrogen-saturated aqueous solutions of 0.1 mol dm^-1 KOH. A substantial activation by potential cycling of the pristine catalysts synthesized by solvothermal reduction is necessary before these become active for the HOR; in situ Raman spectroscopy shows that after activation the surface of the Ni/C, Ni₃Fe, and Ni₃Co catalysts is fully reduced at 0 V, whereas the surface of the Ni₃Cu catalyst is not. The activation procedure had a smaller but negative impact on the catalysts synthesized by chemical reduction. After activation, the exchange-current densities normalized with respect to the ECSA (electrochemically active surface area) were approximately independent of composition but relatively high compared to catalysts of larger particle diameter.