The biocompatibility and mineralization potential of mineral trioxide aggregate containing calcium fluoride-An
Miyoung Lim1, Minju Song2, Chan-Ui Hong2
1Department of Conservative Dentistry, Dankook University College of Dentistry Jukjeon Hospital, Yongin, South Korea.
Background/Purpose:
MTA is used to induce hard tissue regeneration in various procedures. This study evaluated the biocompatibility and mineralization potential of mineral trioxide aggregate (MTA) containing calcium fluoride (CaF2). To verify if the change of components affected physical properties, the setting time, solubility, and surface roughness were measured.
Materials And Methods:
Human dental pulp cells (HDPCs) were treated with powder and set MTA containing CaF2 (0, 1, 5, and 10 wt %). The proliferation of HDPCs was investigated using 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. The mineralization potential of HDPCs was investigated with the relative gene expression of alkaline phosphatase (ALP), collagen type I (ColI), osteocalcin (OCN), and runt-related transcription factor 2 (Runx2) using real-time reverse transcription polymerase chain reaction (RT-PCR). For investigating the physical properties, setting time and solubility were tested. Surface profiles of material were analyzed by a non-contact surface profiler and a scanning electron microscope (SEM).
Results:
MTA-5% CaF2 mixtures increased the proliferation and the mineralization-related gene expression of HDPCs to a greater degree than pure MTA. The addition of CaF2 to MTA delayed the setting, but the difference was only significant in the MTA-10% CaF2. Solubility and surface roughness was not altered.
Conclusion:
The addition of more than 5% CaF2 can be considered to increase the regeneration potential of pulp cells without adverse effects on physical property.