Development and characterization of experimental ZnO cement containing niobophosphate bioactive glass as filling...

The aim of this study was to develop and characterize a temporary restorative material based on a zinc oxide matrix containing niobophosphate bioactive glass (NbG) for the caries-affected dentin treatment.

NbG was added to a ZnO₂ matrix in different concentrations (wt%). EDS-SEM, ATR-FTIR and XRD analyses were performed to characterize the cement. Calcium release was evaluated in TRIS solution after 1, 7 and 14 days by colorimetric method (A₆₅₀). Compressive strengths and setting times were performed to analyze mechanical properties.

EDS spectra confirmed the presence of Ca, P and Nb in the groups containing NbG. EDS mapping exhibit the ZnO₂ homogeneous distribution, and NbG immersed in this matrix. Peaks suggesting interaction between matrix and NbG were not detected in Ftir spectra. Calcium releasing showed to be time-dependent for experimental groups containing 10, 20, 30 and 40%. The NbG incorporation progressively increased the compressive strength values in the experimental groups. NbG incorporation seemed to influence the ZnO₂ matrix early setting reaction. No statistical difference was observed in the final setting time.

The addition of NbG particles into zinc oxide matrix could work as a mechanical reinforcement. It is suggested that the calcium released by the cement containing at least 10% NbG could induce apatite formation.