Early-Age Mechanical Properties of 3D-Printed Mortar with Spent Garnet

Szymon Skibicki1, Patrycja Jakubowska1, Maria Kaszyńska1

  • 1Faculty of Civil and Environmental Engineering, West Pomeranian University of Technology in Szczecin, Piastów 50a, 70-311 Szczecin, Poland.

Materials (Basel, Switzerland)
|January 11, 2022
PubMed

Keywords:
3D concrete3D mortaraggregate replacementfine aggregate replacementgarnet wastenatural sand replacementrecycled aggregatespent garnetsustainability3D printing mortarspent garnet replacementgreen strengthYoung's modulussustainable construction

More Related Videos

Micro-masonry for 3D Additive Micromanufacturing08:45

Micro-masonry for 3D Additive Micromanufacturing

Published on: August 1, 2014

10.5K
Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography06:53

Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography

Published on: January 25, 2019

14.6K

Related Concept Videos

Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
207
Mortar01:29

Mortar

Mortar, a mixture of Portland cement, hydrated lime, sand, and water, is a crucial binding material in construction. Its primary function is to join masonry units together, filling gaps and ensuring a uniform distribution of weight across the structure. This helps in preventing potential weaknesses. Mortar also serves as a protective barrier against environmental elements such as water and wind, thereby safeguarding the interior of the structure. It also compensates for surface irregularities...
343
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
237
Mortar Joint Deterioration in Masonry01:13

Mortar Joint Deterioration in Masonry

Mortar joint deterioration is a significant concern in masonry structures, with water accumulation in the joints leading to damage from freeze-thaw cycles. The repeated expansion of water during freezing and its melting during thawing develop and propagate cracks in the masonry joints. Eventually, this leads to the spalling of mortar from the joints, loosening masonry units and weakening the structure. The deteriorated mortar joints are also vulnerable to moisture intrusion into the walls.
The...
174
Mortar Joints in Brick Masonry01:25

Mortar Joints in Brick Masonry

Mortar joints play a critical role in brick masonry, filling the spaces between brick to bind them together and provide structural integrity and strength. The thickness of these joints is variable, typically ranging from less than one-fourth inch to over half an inch, based on structural needs and specific applications.
The process of joint tooling is implemented as the mortar begins to harden. This technique involves compacting and shaping the mortar to enhance both the appearance and the...
209
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...