Novel Heteroleptic Tin(II) Complexes Capable of Forming SnO and SnO2 Thin Films Depending on Conditions Using
Seong Ho Han1,2, Raphael Edem Agbenyeke1,3, Ga Yeon Lee1,2
1Thin Film Materials Research Center, Korea Research Institute of Chemical Technology, 141 Gajeong-ro, Yuseong-gu, Daejeon 34114, Republic of Korea.
Abstract:
A new heteroleptic complex series of tin was synthesized by the salt metathesis reaction of SnX2 (X = Cl, Br, and I) with aminoalkoxide and various N-alkoxy-functionalized carboxamide ligands. The complexes, [ClSn(dmamp)]2 (1), [BrSn(dmamp)]2 (2), and [ISn(dmamp)]2 (3), were prepared from the salt metathesis reaction of SnX2 with one equivalent of dmamp; [Sn(dmamp)(empa)]2 (4), [Sn(dmamp)(mdpa)]2 (5), and [Sn(dmamp)(edpa)]2 (6) were prepared via the salt metathesis reaction using complex 2 with one equivalent of N-alkoxy-functionalized carboxamide ligand. Complexes 1-5 displayed dimeric molecular structures with tin metal centers interconnected by μ2-O bonding via the alkoxy oxygen atom. The molecular structures of complexes 1-5 showed distorted trigonal bipyramidal geometries with lone pair electrons in the equatorial position. Using complex 6 as a tin precursor, SnO films were deposited by chemical solution deposition (CSD) and subsequent post-deposition annealing (PDA) at high temperatures. SnO and SnO2 films were selectively obtained under controlled PDA atmospheres of argon and oxygen, respectively. The SnO films featured a tetragonal romarchite structure with high crystallinity and a preferred growth orientation along the (101) plane. They also exhibited a lower transmittance of >52% at 400 nm due to an optical band gap of 2.9 eV. In contrast, the SnO2 films exhibited a tetragonal cassiterite crystal structure and an extremely high transmittance of >97% at 400 nm was observed with an optical band gap of 3.6 eV.