Discussion of Orientation and Performance of Crosslinked Ultrahigh-Molecular-Weight Polyethylene Used for Artificial...

Previously, the orientation structure of ultrahigh-molecular-weight polyethylene (UHMWPE) for artificial joints was considered to be unchanged after irradiation crosslinking. Therefore, much of the research related to the long-term failure of artificial joints has focused on material improvements. In this study, ultrasmall-angle X-ray scattering (USAXS) and the small/wide-angle X-ray scattering (SAXS-WAXS) combined technique reveal that the orientation structures of UHMWPE materials at all scales (nanoscale to microscale) are responsible for the long-term failure of artificial joints. To further illustrate the formation of these hierarchical oriented structures, a simple model is presented. In this model, first, the migration of free radicals plays a vital role, and the different steric hindrances in different directions directly lead to uneven migration behavior of free radicals. Second, the uneven migration of free radicals contributes to an inhomogeneous concentration of free radicals, thus resulting in observable crosslinking nonuniformities. Finally, all the hierarchical structural nonuniformities promote long-term failure of artificial joints after long-term wear.