Facile synthesis of ZIF-67 derived dodecahedral C/NiCO₂S₄ with broadband microwave absorption performance

The increasing hazard of electromagnetic radiation prompts people to pursue absorbing materials with better performance. However, absorbing materials with a single loss mechanism usually is unable to obtain better absorbing performance due to low impedance matching or high filling ratio. Therefore, this work proposes a C/NiCo₂S₄ (CNCS) material with both dielectric loss/magnetic loss to achieve efficient absorption of electromagnetic waves. The simple preparation of CNCS materials was achieved through the etching of the ZIF-67 template by nickel nitrate and the subsequent hydrothermal vulcanization process. Its unique prismatic dodecahedron hollow structure promotes multiple scattering of electromagnetic waves. The attachment of the magnetic NiCo₂S₄ particles on the surface of the carbon template further promotes the interface polarization and dipole polarization, which is equivalent to the formation of a resistance-rich microcircuit and enhances the effect of the conductance loss on electromagnetic waves. At 2-18 GHz, the CNCS-2 with 30% paraffin addition achieves an effective bandwidth of 5.54 GHz at a matching thickness of 1.7 mm, and has a maximum reflection loss of -36.44 dB at 1.5 mm. By adjusting the thickness of the material matching layer (1-3 mm), an effective bandwidth of up to 13.48 GHz can be achieved, perfectly covering the X-band and Ku-band. Based on the simple preparation process of the material, the special hollow structure and the multiple loss mechanisms for electromagnetic waves, we believe that CNCS can become a strong competitor for high-efficiency broadband absorbers.