A post-deposition annealing approach for organic residue control in TiO₂ and its impact on Sb₂Se₃/TiO₂ device...

We report a systematic investigation on the influence of two-step post-deposition treatments (PDTs) on TiO₂ buffer layers deposited by ultrasonic spray pyrolysis (USP) for emerging Sb₂Se₃ photovoltaics. Air annealing is a typical method for recrystallizing chemically deposited TiO₂ films. However, organic residues (such as carbon species) from a precursor solution based on titanium tetraisopropoxide and acetylacetone may still remain on the TiO₂ surface, therefore requiring an additional annealing step. We demonstrate that vacuum annealing can be a suitable technological approach to decrease the concentration of carbon species in TiO₂ films. Vacuum annealing was performed at temperatures at 160-450 °C prior to the 450 °C air annealing step. It was found that vacuum annealing at 160 °C followed by subsequent air annealing led to better device performance. This was explained by achieving an optimal balance between the removal of carbon content during vacuum annealing and the active recrystallization of TiO₂ during air annealing. The decrease of carbon concentration by employing the two-step approach was supported by changes in the lattice parameters of TiO₂ and proven by X-ray photoelectron spectroscopy (XPS). The given study provides experimental evidence on how nanoscale carbon species in the TiO₂ heterojunction partner layer of a Sb₂Se₃ solar cell can affect the device's performance. By this approach, we generate complementary insights on how the quality of the main interface has an impact and can take a key role despite the optimized Sb₂Se₃ grain structure and orientation.