Effect of the Oxidation Process on Carrier Lifetime and on SF Defects of 4H SiC Thick Epilayer for Detection...

The aim of this work was a deep spectroscopical characterization of a thick 4H SiC epitaxial layer and a comparison of results between samples before and after a thermal oxidation process carried out at 1400 °C for 48 h. Through Raman and photoluminescence (PL) spectroscopies, the carrier lifetimes and the general status of the epilayer were evaluated. Time-resolved photoluminescence (TRPL) was used to estimate carrier lifetime over the entire 250 µm epilayer using different wavelengths to obtain information from different depths. Furthermore, an analysis of stacking fault defects was conducted through PL and Raman maps to evaluate how these defects could affect the carrier lifetime, in particular after the thermal oxidation process, in comparison with non-oxidated samples. This study shows that the oxidation process allows an improvement in the epitaxial layer performances in terms of carrier lifetime and diffusion length. These results were confirmed using deep level transient spectroscopy (DLTS) measurements evidencing a decrease in the Z_1/2 centers, although the oxidation generated other types of defects, ON1 and ON2, which appeared to affect the carrier lifetime less than Z_1/2 centers.